In this study, the effects of incorporating recycled photopolymer-plate residues from a packaging flexography process into polyester-glass fiber composites were examined. Ternary composites with an unsaturated polyester matrix with elastomer particles from recycled photopolymer-plate residues were evaluated using two types of glass fibers: in the forms of a fabric with bidirectional fibers and a blanket with multidirectional fibers. The composites were prepared by hand lay-up lamination using different rubber contents (0, 2.5, 5, and 10 wt% based on the polyester resin mass fraction), and were characterized for their void content, flexural and impact strengths, and dynamic mechanical properties. Primary results indicated that the incorporation of the rubber particles increased the difficulty of lamination, while promoting greater void formation with higher filler content. The rubber particles decreased the impact resistance properties but did not reduce the flexural strength or storage modulus, indicating that despite the elastomeric composition, this residue from the photopolymer plates showed a reinforcing rather than toughening character.

This study focuses on the use of waste cotton fiber from the textile industry to produce composites with unsaturated polyester and to evaluate the performance of glass (G) / cotton (C) fiber laminates, particularly their mechanical and dynamic mechanical properties. Distinct stacking sequences were studied but the overall fiber content was kept constant. In general, hybrid laminates exhibited intermediate mechanical properties compared to those of the pure laminates, and optimum performance was obtained when the glass fiber mats were placed on the surfaces of the composite. Furthermore, some hybrid laminates exhibited superior dynamic mechanical performance, even compared to the pure glass laminate. Lower tan delta peak height (related to better fiber-matrix interaction) values and higher Tg were reported for the [C/G/ G ¯]s and [G/C/ C ¯]s samples which, together with the [G/C/ G ¯]s sample, exhibited the best results for reinforcement effectiveness and loss modulus peak height. Therefore, it is found possible to partially replace the glass fiber by waste cotton fiber considering that the final product may be optimized for mechanical property, which requires glass fiber at the surface of the laminate, or for dynamic mechanical properties, that allows higher cotton fiber content.

The use of ramie fibers as reinforcement in hybrid composites is justified considering their satisfactory mechanical properties if compared with other natural fibers. This study aims to verify changes in chemical composition and thermal stability of the ramie fibers after washing with distilled water. One additional goal is to study glass fiber and washed ramie fiber composites focusing on the effect of varying both the fiber length (25, 35, 45 and 55 mm) and the fiber composition. The overall fiber loading was maintained constant (21 vol.%). Based on the results obtained, the washed ramie fiber may be considered as an alternative for the production of these composites. The higher flexural strength presented being observed for 45 mm fiber length composite, although this difference is not significant for lower glass fiber volume fractions: (0:100) and (25:75). Also, by increasing the relative volume fraction of glass fiber until an upper limit of 75%, higher flexural and impact properties were obtained.